- High Cold and Radiation Resistant Silicone Rubber
High Cold and Radiation Resistant Silicone Rubber

- Resists embrittlement even at -100℃ and has excellent low-temperature properties.
- It has low compression set and excellent sealing properties, especially at low temperatures.
- Excellent resistance to radiation such as gamma rays.
- Hardness is 30 and 60 (Durometer A)

Product Information
Key Points
Use | For molding |
---|---|
Molding method | Extrusion molding, press molding, peroxide curing |
Features | Cold resistant |
Industries | Automobiles, transport, aircraft, space, infrastructure, general industry |
Application
- Materials that require high cold resistance
- Materials that require low temperature resistance and radiation resistance in the aircraft and space fields
- Components for low-temperature warehouses, equipment used in cold regions, and other general industrial components

Expected Results
- Excellent cold resistance →Can be used in low temperature environments where organic rubbers cannot.
- Excellent moldability →Can be compressed and extruded.
- Low compression set → Maintains excellent sealing properties even in low temperature environments
- Radiation resistance → Suitable for use in the aerospace industry
Parameter\Product name | KE-183-U | KE-186-U | |||
---|---|---|---|---|---|
Appearance | Milky white translucent | Milky white translucent | |||
Williams plasticity (10 min after remix) | 189 | 277 | |||
Standard adding quantity phr |
Curing agent name | C-23N 0.7 | C-8 2.0 | C-23N 0.7 | C-8 2.0 |
Test piece standard curing conditions |
Primary cure Post cure |
120℃×10m 200℃×4h |
160℃×10m 200℃×4h |
120℃×10m 200℃×4h |
160℃×10m 200℃×4h |
Hardness (Durometer A) | 31 | 36 | 62 | 65 | |
Density at 23℃ (g/cm3) | 1.11 | 1.12 | 1.19 | 1.19 | |
Tensile strength (MPa) | 8.7 | 8.2 | 11.2 | 11.0 | |
Elongation at break (%) | 640 | 550 | 570 | 480 | |
Tear strength Crescent piece (kN/m) | 10 | 8 | 25 | 19 | |
Compression set 150℃×22h (%) | 14 | 6 | 23 | 12 | |
Modulus of resilience (%) | 53 | 64 | 41 | 46 |
(Not specified values)
Temperature and Elasticity of Silicone Rubber
・It does not lose its rubber elasticity even in low temperatures of -100℃.
Radiation Dose and Elongation at Break
・Compared to general silicone rubber, changes in rubber properties due to radiation are minimal, and it has excellent radiation resistance.