Self-adhesive LIMS (General Purpose)

- Primer is not required and it self-adheres to resin and metal without adhesive.
- It can adhere to a wider variety of resins and metals than our conventional products.
- Injection molding allows for automation of molding.
- Hardness range from 40 to 60 (Durometer A).

Product Information
Key Points
Use | For molding |
---|---|
Molding method | Injection molding, addition curing |
Features | Self-adhesive, resin adhesive, metal adhesive, high strength, fast curing, reduced low-molecular-weight siloxane |
Industries | General industry, automotive, transport, electrical and electronics |
Application
- Parts for which productivity needs to be improved through two-color molding
- Waterproof seals and other components that require reliable adhesion
- Integral molding of resin and metal

Expected Results
- Bonds to resin and metal without adhesives or primers → Shortens bonding process and improves reliability
- Can be bonded to various types of resins and metals → Can be used universally.
Parameter\Product name | KE-2098 -40-A/B |
KE-2098 -50-A/B |
KE-2098 -60-A/B |
|
---|---|---|---|---|
Appearance | Translucent | Translucent | Translucent | |
Viscosity A/B (Pa・s:0.9s-1) |
819/797 | 890/850 | 870/790 | |
Curing speed at 130℃ (MDR) |
T10 | 23 | 24 | 22 |
T90 | 60 | 54 | 47 | |
Test piece standard curing conditions |
Primary cure | 150℃×5min | 150℃×5min | 150℃×5min |
Post cure | Not required | Not required | Not required | |
Density at 23℃ (g/cm3) | 1.14 | 1.15 | 1.14 | |
Hardness (Durometer A) | 40 | 47 | 61 | |
Elongation at break (%) | 700 | 610 | 430 | |
Tensile strength (MPa) | 9.2 | 8.5 | 8.9 | |
Tear strength Crescent piece (kN/m) | 35 | 36 | 42 |
(Not specified values)
Shear Adhesive Strength of KE-2098-40-A/B to Various Substrates
* Can be bonded to a wide variety of resins and metals.