Flame Retardancy

When the added resin burns, it quickly migrates to the burning surface to form a flame retardant layer on the surface, preventing the spread of fire.
Results 33
X-40-9309A

X-40-9309A
- This product contains UV absorber to prevent UV degradation of base material.
- This product cures at room temperature.
- One-component type (contains curing catalyst)
- This product forms high hardness coating film.
X-40-2756

X-40-2756
- Addition cure type
- One-component product containing curing catalyst
- Low curing shrinkage enables molded products and thick films
- Good adhesion to glass substrates
X-48-1030

X-48-1030
- TX (toluene, xylene)-free type; uses PGMAC solvent
- Excellent heat resistance
- High hardness
- Proven mainly as a binder for heat-resistant paints
X-88-1007

X-88-1007
- Good adhesion to hard-to-bond base materials such as SUS and acrylic
- Good crack resistance and water repellency
X-88-1004

X-88-1004
- Good adhesion to hard-to-bond base materials such as SUS and acrylic
- High hardness and good scratch resistance
X-48-1600

X-48-1600
- This product has high hardness and flexural resistance.
- Since this product cures by de-ethanol reaction, it is environmentally friendly.
X-48-1500

X-48-1500
- This product has high hardness and flexural resistance.
- Rapid curing
X-40-9312

X-40-9312
- High hardness and crack resistance
- Excellent resistance to yellowing and cracking after
KR-4000G

KR-4000G
- One-component type
- High gloss
- Excellent water repellency and water sliding properties
- Exhibits antifouling performance even when wiped off.
X-40-2327

X-40-2327
- Fast curing
KR-400

KR-400
- Standard product of one-component type (containing curing catalyst)
- High hardness
KR-401

KR-401
- Excellent flexural resistance
- High gloss
KR-213

KR-213
- For resin modification
- Can add flexibility and crack resistance
KR-510

KR-510
- Standard product of methyl/phenyl type
- Modifying heat resistance and weather resistance of organic resins
- This product imparts flexibility and crack resistance to silicone oligomer based coating agents.
KR-401N

KR-401N
- This product forms flexible cured film.
- High gloss
- Not containing curing catalyst
(KR-401 is containing curing catalyst)
KR-400N

KR-400N
- High hardness
- KR-400N is made from KR-400 without curing catalysis.
KR-2710

KR-2710
- Flame retardant agents for polycarbonate
- Good transparency
X-40-9246

X-40-9246
- Good crack resistance
- This product has been used as binder for coating agents and modifier for organic resins.
X-40-9250

X-40-9250
- This product has flexibility owing to the introduction of D unit.
- This product has excellent water repellency and water slip properties
- This product has been used as a coating binder.
KR-220L

KR-220L
- Solid (100% silicone content) in flake form
- This product has been used as resistor paints, binders for sintered metal powder, etc.
- Less smoke generation
X-40-9225

X-40-9225
- Higher molecular weight than KR-500
- Contains only T units
- This product has been used as binder for coating agents and modifier for organic resins.
KR-500

KR-500
- Higher molecular weight than KR-515
- Made up of T units only
- Standard product in methyl type
- This product has been used as binder for coating agents and modifier for organic resins.
KR-515

KR-515
- Higher molecular weight than KC-89S
- Contains only T units
- This product has been used as binder for coating agents and modifier for organic resins.
KC-89S

KC-89S
- This product contains only T units.
- This product forms high hardness cured film.
- This product has been used as binder for coating agents.
KR-480

KR-480
- This product is developed as a flame-retardant agent for polycarbonate.
- This product has many phenyl groups and good compatibility with organic resins
- This product has almost no Si-OH groups and is thermoplasticity.
- This product has been used as a stress-release agent for epoxy molding.
X-40-2667A

X-40-2667A
- Addition cure type
- Two-component type consisting of a main agent (X-40-2667A) and a curing agent (X-40-2667B)
- Low curing shrinkage enables molded products and thick films
- Good adhesion to glass substrates
KR-311

KR-311
- Standard product of methyl/phenyl type
- This product forms cured films with excellent heat resistance.
- Good compatibility with organic resins
- This product has been mainly used as a binder for heat-resistant paints.
KR-300

KR-300
- This product forms cured film with excellent heat resistance.
- High hardness
- This product has been mainly used as a binder for heat-resistant paints.
KR-282

KR-282
- This product forms cured film with excellent heat resistance.
- Minimal cracking and peeling at high temperatures, good balance of performance
- This product has been mainly used as a binder for heat-resistant paints.
KR-271

KR-271
- This product forms cured film with excellent heat resistance and electrical insulation.
- Flexibility and less cracking and peeling at high temperatures
- This product has been mainly used as a binder for coatings and paints.
KR-255

KR-255
- Even at room temperature, when the solvent volatilizes, a lacquer film is formed.
- Heating further forms a film with excellent heat resistance and chemical resistance
- This product has been mainly used as coatings with electrical insulation and water resistance.
KR-242A

KR-242A
- This product forms high hardness film.
- Less smoke generation when heated
- This product has been mainly used as binders of inorganic materials (i.e. mica).
KR-220LP

KR-220LP
- Solid (100% silicone content) and powdered
- KR-220L further ground and powdered
- Less smoke generation