• Very high reactivity of alkoxy group and rapid curing
• Alkali resistance
• Water resistance

• Alkali resistance
• Water resistance

• This product contains UV absorber to prevent UV degradation of base material.
• This product cures at room temperature.
• One-component type (contains curing catalyst)
• This product forms high hardness coating film.

• Acrylic equivalent 330g/mol
• This product imparts flexural resistance to acrylic resins.
• This product has excellent compatibility with acrylic resins and various photoinitiators.
• This product is applicable to UV/EB curing systems.

• Relatively low molecular weight and excellent compatibility with epoxy resins
• Good leveling and wettability with linear siloxane structure
• Low viscosity and effective as a reactive diluent

• Addition cure type
• One-component product containing curing catalyst
• Low curing shrinkage enables molded products and thick films
• Good adhesion to glass substrates

• TX (toluene, xylene)-free type; uses PGMAC solvent
• Excellent heat resistance
• High hardness
• Proven mainly as a binder for heat-resistant paints

• This product can be used by simply cold-blend*.
• Applicable organic resins are silicone-modified acrylic polymers/polyesters/alkyds/weak solvent acrylic resins/NAD.
• This product improves weather resistance, heat resistance, anti-marking pen fouling properties, acid/alkali resistance, etc..
• Recommended additive amount is 10~50 parts per 100 parts resin solid content.

* Cold blend: A method of blending by simply mixing without heating

• It can be used in combination with isocyanate curing agents.
• This product can be used by simply cold-blend*.
• Recommended additive amount is 3% to 20% (NCO equivalent) of catalyst.
• This product improves weather resistance and oil repellency.
• Applicable polyols are silicone-modified acrylic/polyesters/alkyd polyols.

* Cold blend: A method of blending by simply mixing without heating

• Good adhesion to hard-to-bond base materials such as SUS and acrylic
• Good crack resistance and water repellency

• Good adhesion to hard-to-bond base materials such as SUS and acrylic
• High hardness and good scratch resistance

• This product has high hardness and flexural resistance.
• Since this product cures by de-ethanol reaction, it is environmentally friendly.

• This product has high hardness and flexural resistance.
• Rapid curing

• Ultra high molecular weight
• Even at room temperature, when the solvent volatilizes, a lacquer film is formed.
• Heating further forms a film with excellent heat resistance and chemical resistance
• This product has been mainly used as coatings with electrical insulation and water resistance.

• High hardness and crack resistance
• Excellent resistance to yellowing and cracking after

• Relatively low molecular weight and excellent compatibility with epoxy resin
• Low shrinkage during curing due to cyclic siloxane structure

• One-component type
• High gloss
• Excellent water repellency and water sliding properties
• Exhibits antifouling performance even when wiped off.

• Standard product of one-component type (containing curing catalyst)
• High hardness

• Alkoxy groups are methoxy groups and ethoxy groups.
• Mercapto equivalent 800g/mol

• Fast curing

• Excellent flexural resistance
• High gloss

• For resin modification
• Can add flexibility and crack resistance

• Alkoxy groups are methoxy groups and ethoxy groups.
• Epoxy equivalent 830g/mol

• Alkoxy groups are methoxy groups.
• Epoxy equivalent 590g/mol

• Alkoxy groups are methoxy groups.
• The organic functional groups have methyl groups in addition to the epoxy groups.
• Epoxy equivalent 280g / mol

• UV curable, good curability under air
• Contains UV absorbers for superior weather resistance
• Low viscosity, excellent scratch resistance and low warpage
• Compatible with coating methods that require low viscosity, such as spray coating

• Alkoxy groups are methoxy groups.
• Organic substituent has both methyl group as well as mercapto group
• Mercapto equivalent 450g/mol

• Alkoxy groups are methoxy groups.
• Acrylic equivalent 210g/mol
• Applicable to UV/EB curing system
• Lower volatility than KBM-5103 (monomer type)

• Reactive functional groups are methacrylic groups.
• Methacryl equivalent 230g/mol
• Applicable to UV/EB curing system

• Reactive functional groups are Vinyl groups.
• Vinyl equivalent 530g/mol
• Flame retardant for Polycarbonate

• Relatively low molecular weight and excellent compatibility with epoxy resin
• Less shrinkage during curing due to cyclic siloxane structure
• Good crack resistance due to di-functionality

• Solid (100% silicone content) in flake form
• This product has been used as resistor paints, binders for sintered metal powder, etc.
• Less smoke generation

• This product has the heat resistance of silicone resin and the room temperature curability of alkyd resin.

• Solid (100% silicone content) and powdered
• KR-220L further ground and powdered
• Less smoke generation

• This product forms high hardness film.
• Less smoke generation when heated
• This product has been mainly used as binders of inorganic materials (i.e. mica).

• Excellent heat shock resistance
• Heat resistance and releasability

This product has been mainly used as coating and paint applications.

• Modifier of organic resins
• Adding heat resistance and weather resistance are possible.
• This product has been mainly used as paint applications.

• Modifier for organic resins
• More compatibility and flexibility than KR-211
• Adding heat resistance and weather resistance
• This product has been mainly used as paint applications.

• Even at room temperature, when the solvent volatilizes, a lacquer film is formed.
• Heating further forms a film with excellent heat resistance and chemical resistance
• This product has been mainly used as coatings with electrical insulation and water resistance.

• This product forms cured film with excellent heat resistance and electrical insulation.
• Flexibility and less cracking and peeling at high temperatures
• This product has been mainly used as a binder for coatings and paints.

• This product forms cured film with excellent heat resistance.
• Minimal cracking and peeling at high temperatures, good balance of performance
• This product has been mainly used as a binder for heat-resistant paints.

• This product forms cured film with excellent heat resistance.
• High hardness
• This product has been mainly used as a binder for heat-resistant paints.

• Standard product of methyl/phenyl type
• This product forms cured films with excellent heat resistance.
• Good compatibility with organic resins
• This product has been mainly used as a binder for heat-resistant paints.

• Addition cure type
• Two-component type consisting of a main agent (X-40-2667A) and a curing agent (X-40-2667B)
• Low curing shrinkage enables molded products and thick films
• Good adhesion to glass substrates

• Standard product of methyl/phenyl type
• Modifying heat resistance and weather resistance of organic resins
• This product imparts flexibility and crack resistance to silicone oligomer based coating agents.

• This product has the heat resistance of silicone resin and the chemical resistance, flex resistance, and high gloss of polyester resin.
• This is a standard product of polyester resin modified series.

• This product has the heat resistance of silicone resin and the chemical resistance, flex resistance, and high gloss of polyester resin.
• Faster curing speed compared to KR-5230

• This product has the heat resistance of silicone resin and the chemical resistance, bending resistance, and high gloss of polyester resin.
• Owing to the non-stich property, this product has been used as heat resistant paints for kitchen area.

• This product contains only T units.
• This product forms high hardness cured film.
• This product has been used as binder for coating agents.

• Higher molecular weight than KC-89S
• Contains only T units
• This product has been used as binder for coating agents and modifier for organic resins.

• Higher molecular weight than KR-515
• Made up of T units only
• Standard product in methyl type
• This product has been used as binder for coating agents and modifier for organic resins.

• Higher molecular weight than KR-500
• Contains only T units
• This product has been used as binder for coating agents and modifier for organic resins.
  

• Good crack resistance
• This product has been used as binder for coating agents and modifier for organic resins.

• This product has flexibility owing to the introduction of D unit.
• This product has excellent water repellency and water slip properties
• This product has been used as a coating binder.

• High hardness
• KR-400N is made from KR-400 without curing catalysis.

• This product forms flexible cured film.
• High gloss
• Not containing curing catalyst
  (KR-401 is containing curing catalyst)