Adhesion

Mainly due to the effect of reactive functional groups such as alkoxy, it improves adhesion at various interfaces such as between inorganic substrates and resins.
Results 73
X-12-1307

X-12-1307
- Silane coupling agent with mercapto group
- Shorter spacer chain compared to general-purpose products,
Higher hydrolysis - Adhesion improvement can be expected.
X-12-1287A

X-12-1287A
- Silane coupling agent with butadiene backbone, acid anhydride structure, and trimethoxysilyl groups
- Butadiene backbone improves compatibility with rubber materials, and can also impart hydrophobicity.
- With trimethoxysilyl groups and acid anhydride functional groups, it can be expected to have a high adhesive effect.
X-88-1007

X-88-1007
- Good adhesion to hard-to-bond base materials such as SUS and acrylic
- Good crack resistance and water repellency
KBM-585

KBM-585
- Silane coupling agent with ureido groups
- Excellent effect on amide resins, etc. can be expected.
X-48-1801

X-48-1801
- It can be used in combination with isocyanate curing agents.
- This product can be used by simply cold-blend*.
- Recommended additive amount is 3% to 20% (NCO equivalent) of catalyst.
- This product improves weather resistance and oil repellency.
- Applicable polyols are silicone-modified acrylic/polyesters/alkyd polyols.
* Cold blend: A method of blending by simply mixing without heating
X-88-1004

X-88-1004
- Good adhesion to hard-to-bond base materials such as SUS and acrylic
- High hardness and good scratch resistance
KBE-585A

KBE-585A
- Silane coupling agent with ureido groups, alcohol (methanol, ethanol) solution of about 50% active ingredient
- Excellent effect on amide resin, etc. can be expected.
POLON-V8

POLON-V8
- Due to the quaternary ammonium salt structure, antimicrobial and antiviral properties can be expected.
- Much higher stability in aqueous solution due to the characteristics of the molecular structure
- Uses ethanol solvent with lower environmental impact
- Adhesion improvement to fibers can be expected.
- Improved washing durability can be expected.
X-12-1048

X-12-1048
- Silane coupling agent with acrylic groups and intramolecular polar structure
- Improved coupling performance due to polar structure
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
X-12-1333A

X-12-1333A
- Silane coupling agent with cyclization polymerization properties
- Superior thermal degradability and adhesiveness compared to KBM-503 and KBM-5103
- Silane coupling agent with acrylic groups as organic functional groups
- This product is used for processing silica.
KBM-1403

KBM-1403
- Silane coupling agent with styryl groups
- Since it contains styrene groups, anionic, cationic, and radical polymerization are possible
- By adding it to polymerizable resin compositions, it is expected to improve the adhesion between inorganic materials such as fillers and resin.
X-12-1056ES

X-12-1056ES
- Silane coupling agent with silyl group-protected mercapto groups
This product can be mixed with materials that cannot be mixed with mercaptosilane. - Stability improvement of compositions (epoxy, acrylic, isocyanate) and adhesion improvement can be expected.
- Odor improvement peculiar to mercapto groups can be expected.
X-12-1290

X-12-1290
- Silane coupling agent with allyl isocyanurate structure
- Radical cross-linking is possible due to the presence of allyl groups
- By adding to polymerizable resin compositions, it is expected to improve the adhesion between inorganic materials such as fillers and resin.
X-12-1214A

X-12-1214A
- Silane coupling agent with benzotriazole groups
- This product has anti rust properties.
Combined with the adhesion of silane coupling agents, long lasting anti rust properties can be expected.
KBM-503

KBM-503
- Silane coupling agent with methacrylate groups
- This product is used for treatment of silica
- This product is used for resin concrete, polyester FRP, and dental materials.
X-12-989MS

X-12-989MS
- Chelating-type silane coupling agent with heterocyclic ring
- Through non-bonding interactions with active hydrogen and metal ions, adhesion improvement to inorganic materials (i.e. metals) can be expected.
- Since this product does not have reactive groups, it does not have adverse effects on the composition.
X-12-967C

X-12-967C
- Silane coupling agent with acid anhydride
- Improved stability of compositions and adhesion (polyimide etc.) can be expected.
KR-513

KR-513
- Alkoxy groups are methoxy groups.
- Acrylic equivalent 210g/mol
- Applicable to UV/EB curing system
- Lower volatility than KBM-5103 (monomer type)
KR-519

KR-519
- Alkoxy groups are methoxy groups.
- Organic substituent has both methyl group as well as mercapto group
- Mercapto equivalent 450g/mol
X-12-1126

X-12-1126
- Aqueous silane coupling agent with quaternary ammonium salts
- Saves on hydrolysis process as it has already been hydrolyzed
- Nonflammable, reduced VOC generation
- Sustainable antimicrobial properties can be expected by fixing on the surface of fibers and inorganic materials.
KBE-1003

KBE-1003
- Vinyl group silane coupling agent compatible with polyethylene, polypropylene, etc.
- Mainly used to improve heat resistance of polyethylene for electric wires
- This product is used for cross-linked polyethylene
KBM-1003

KBM-1003
- Vinyl group silane coupling agent compatible with polyethylene, polypropylene, etc.
- Mainly used to improve heat resistance of polyethylene for electric wires
- This product is used for cross-linked polyethylene
KBM-1083

KBM-1083
- Silane coupling agent with vinyl group and longer spacer chain than conventional product (KBM-1003)
- Owing to the long spacer chain, improvement of hydrophobicity and flexibility can be expected.
- Improvement of high filler filling, flexibility of cured material, alkali resistance, water resistance can be expected.
X-12-1267B

X-12-1267B
- Silane coupling agent with butadiene polymer structure as the main backbone
- Butadiene polymer backbone is expected to improve compatibility and adhesiveness to rubber materials
- With high hydrophobicity, improving water resistance can be expected.
X-12-1267B-ES

X-12-1267B-ES
- Silane coupling agent with butadiene polymer structure as the main skeleton
- Butadiene polymer skeleton is expected to improve compatibility and adhesiveness to rubber materials
- With high hydrophobicity, improving water resistance can be expected.
KBE-502

KBE-502
- Silane coupling agent with methacrylate group, which is compatible with polyethylene and polypropylene
- This product is used for treatment of silica
- This product is used for resin concrete, polyester FRP, and dental materials
KBE-503

KBE-503
- Silane coupling agent with methacrylate group, which is compatible with polyethylene and polypropylene
- This product is used for treatment of silica
- This product is used for resin concrete, polyester FRP, and dental materials
KBM-502

KBM-502
- Silane coupling agent with methacrylate groups
- This product is used for treatment of silica
- This product is used for resin concrete, polyester FRP, and dental materials.
X-12-1116

X-12-1116
- Chelate-functional silane coupling agent with thiourea bond
- Through non-bonding interactions with active hydrogen and metal ions, adhesion improvement to inorganic materials (i.e. metals) can be expected.
- Since this product does not have reactive groups, it does not have adverse effects on the composition.
KBM-5803

KBM-5803
- Silane coupling agent with methacrylate group and longer spacer chain than conventional product (KBM-503)
- Owing to the long spacer chain, improvement of hydrophobicity and flexibility can be expected.
- Improvement of adhesiveness, high filler filling, flexibility of cured material, alkali resistance, water resistance can be expected.
X-12-1154

X-12-1154
- Silane coupling agent with mercapto groups
This product has more functional groups than monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
KBM-802

KBM-802
- Silane coupling agent with a mercapto group that is compatible with elastomers and rubber
- This product is used as an adhesion aid between epoxy resin and copper, silver, etc.
- This product is used for elastomers.
KBM-803

KBM-803
- Silane coupling agent with a mercapto group that is compatible with elastomers and rubber
- This product is used as an adhesion aid between epoxy resin and copper, silver, etc.
- This product is used for elastomers.
KBM-6103

KBM-6103
- Silane coupling agent with ethylenediamine structure
- Shorter spacer chains compared to general-purpose products
- Adhesion improvement can be expected
X-12-1303MS

X-12-1303MS
- Silane coupling agent with methacryloxy groups
- Shorter spacer chains compared to general-purpose products
- Adhesion improvement can be expected.
KR-518

KR-518
- Alkoxy groups are methoxy groups and ethoxy groups.
- Mercapto equivalent 800g/mol
KBM-9418-40

KBM-9418-40
- Silane coupling agent with quaternary ammonium salt as organic functional group
- Sustainable antimicrobial properties can be expected by fixing on the surface of fibers and inorganic material
X-12-1139

X-12-1139
- Aqueous silane coupling agent with quaternary ammonium salts as organic functional groups
- Hydrolyzing process has already been finished.
It reduces manufacturing cost. - Nonflammable, reduced VOC generation
- Sustainable antimicrobial properties can be expected by fixing on the surface of fibers and inorganic materials.
KR-516

KR-516
- Alkoxy groups are methoxy groups.
- The organic functional groups have methyl groups in addition to the epoxy groups.
- Epoxy equivalent 280g / mol
X-24-9590

X-24-9590
- Alkoxy groups are methoxy groups.
- Epoxy equivalent 590g/mol
X-88-475

X-88-475
- Silane coupling agent with amino acid ester structure
- By surface treatment of glass fiber, adhesion to epoxy resins etc. will be improved.
- This product is used as a terminal modifier for urethane resins to improve adhesion and water resistance.
- Aqueous solution shows neutrality and high stability.
KR-517

KR-517
- Alkoxy groups are methoxy groups and ethoxy groups.
- Epoxy equivalent 830g/mol
KBE-9007N

KBE-9007N
- Silane coupling agents with isocyanate groups
- This product is added to resins (especially urethane resins containing isocyanate groups) as adhesion improvers.
KR-511

KR-511
- Reactive functional groups are Vinyl groups.
- Vinyl equivalent 530g/mol
- Flame retardant for Polycarbonate
X-12-1050

X-12-1050
- Silane coupling agent with acryloxy groups
This product has a larger number of functional groups than the monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
KBM-5103

KBM-5103
- Silane coupling agent with acrylic groups
- This product can be copolymerized with (meth)acrylic compounds.
- This product is used for treatment of silica.
KBP-64

KBP-64
- Aqueous silane coupling agent with ethylenediamine
- Since this product has already hydrolyzed, the hydrolysis process can be eliminated.
- Nonflammable, reduced VOC generation
KBP-90

KBP-90
- Aqueous silane coupling agent with primary amine as organic functional group
- Since this product has already hydrolyzed, the hydrolysis process can be eliminated.
- Nonflammable, reduced VOC generation
KBE-9103P

KBE-9103P
- Silane coupling agent with a ketimine structure
- This product can be mixed with materials that were previously unmixable with aminosilane.
- Aminosilane is formed through deprotection progresses with moisture and water.
- Improved stability of compositions (epoxy) and improved adhesion can be expected.
X-12-1172ES

X-12-1172ES
- Silane coupling agent with ketimine structure.
This product can be mixed with materials that were previously unmixable with aminosilane. - Improved stability of compositions (epoxy, acrylic, isocyanate) and adhesion can be expected.
KBE-903

KBE-903
- Silane coupling agent with primary amine
- Silane coupling agent with amino group that is compatible with a wide range of resins such as nylon and PVC
- This product is used for surface treatment of glass fiber. And it is used as an ingredient for adhesives and heat insulation mats.
X-12-972F

X-12-972F
- Silane coupling agent with primary amino groups
This product has a larger number of functional groups than the monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
KBM-6803

KBM-6803
- Silane coupling agent with ethylenediamine structure and longer spacer chain than conventional product (KBM-603)
- Owing to the long spacer chain, improvement of hydrophobicity and flexibility can be expected.
- Improvement of adhesiveness, alkali resistance and water resistance can be expected.
KBM-573

KBM-573
- Silane coupling agent with aniline structure
- Since this product contains phenyl groups, compatibility with epoxy resins with phenol groups is improved.
- This product is used for laminated plate.
KBM-575

KBM-575
- Vinylbenzyl-type silane coupling agent
- Effective for surface treatment of glass fibers
- 40% methanol solution of active ingredient
KBM-602

KBM-602
- Silane coupling agent with ethylenediamine structure
- By silane treatment, glass fiber and resin can be chemically bonded.
Improving mechanical strength, heat resistance, water resistance and electrical properties can be expected. - This product is used for paints and adhesives.
KBM-603

KBM-603
- Silane coupling agent with ethylenediamine structure
- By silane treatment, glass fiber and resin can be chemically bonded.
Improving mechanical strength, heat resistance, water resistance and electrical properties can be expected. - This product is used for paints and adhesives.
KBM-903

KBM-903
- Silane coupling agent with primary amino groups
- By silane treatment, glass fiber and resin can be chemically bonded.
Improving mechanical strength, heat resistance, water resistance and electrical properties can be expected. - This product is used for adhesives and heat insulation mats.
KBM-3066

KBM-3066
- Dual-end bistrimethoxy type
X-12-1159L

X-12-1159L
- Silane coupling agent with isocyanate groups
This product has a larger number of functional groups than the monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
X-12-1195

X-12-1195
- Isocyanate group-protected silane coupling agent
- This product will be deprotected by heat to form isocyanate groups.
Since isocyanate groups are protected, it can be mixed with compounds and resins that react with isocyanate groups. - Desorption temperature is 200℃ or higher, and ethanol is used as the blocking agent.
X-12-1293

X-12-1293
- Isocyanate group-protected silane coupling agent
- This product will be deprotected by heat to form isocyanate groups.
Since isocyanate groups are protected, it can be mixed with compounds and resins that react with isocyanate groups. - The desorption temperature is 160~180℃, and caprolactam is used as the blocking agent
X-12-1308ES

X-12-1308ES
- Isocyanate group-protected silane coupling agent
- This product will be deprotected by heat to form isocyanate groups.
Since isocyanate groups are protected, it can be mixed with compounds and resins that react with isocyanate groups. - Desorption temperature is 120~140℃, and dimethyl pyrazole is used as a blocking agent
X-40-9296

X-40-9296
- Reactive functional groups are methacrylic groups.
- Methacryl equivalent 230g/mol
- Applicable to UV/EB curing system
KBE-402

KBE-402
- Silane coupling agent with epoxy groups
- This product makes chemically bond with glass fiber and resin.
It improves, strength, heat resistance, water resistance and electrical properties.
KBE-403

KBE-403
- Silane coupling agent with epoxy group
- This product makes chemically bond with glass fiber and resin.
It improves, strength, heat resistance, water resistance and electrical properties.
KBM-303

KBM-303
- Silane coupling agent with epoxy groups
- This product makes chemically bond with glass fiber and resin.
It improves strength, heat resistance, water resistance and electrical properties. - This product has been used in epoxy laminates and MC nylon.
KBM-402

KBM-402
- Silane coupling agent with epoxy groups
- This product makes chemically bond with glass fiber and resin.
It improves, strength, heat resistance, water resistance and electrical properties.
KBM-403

KBM-403
- Silane coupling agent with epoxy groups
- This product makes chemically bond with glass fiber and resin.
It improves, strength, heat resistance, water resistance and electrical properties.
X-12-981S

X-12-981S
- Silane coupling agent with epoxy groups
This product has a larger number of functional groups than the monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
X-12-984S

X-12-984S
- Silane coupling agent with epoxy groups
This product has a larger number of functional groups than the monomer type. - More reaction points with resin improve coupling performance.
- Low volatility reduces the amount of silane blending.
- Since this product has film-forming properties, it can be used as a high functional primer.
- Since this product contains trialkoxysilyl groups, adhesion improvement can be expected.
KBM-4803

KBM-4803
- Silane coupling agent with epoxy group and longer spacer chain than conventional product (KBM-403)
- Owing to the long spacer chain, improvement of hydrophobicity and flexibility can be expected.
- Improvement of adhesiveness, high filler filling, flexibility of cured material, alkali resistance, water resistance can be expected.
X-12-1135

X-12-1135
- Aqueous silane coupling agent with carboxylic acid
- Since this product has already hydrolyzed, the hydrolysis process can be eliminated.
- Nonflammable, reduced VOC generation