X-31-2835-A/B
X-31-2835-A/B cure faster than conventional condensation liquid silicone rubber.
This product bonds well a variety of materials without cure inhibition by sulfer, phosphorous, nitrogen compounds and so on.
Parameter ![]() |
X-31-2835-A/B | |
---|---|---|
By-product gas |
Alcohol | |
Before curing |
Consistensy |
Liquid |
Appearance |
A: milky white/B: milky white | |
Viscosity at 23°C Rotation 10s-1 Pa·s |
38/30 | |
Blend ratio |
100 : 100 | |
Pot life min |
9 | |
Standard curing condition 23°C ± 2°C/50 ± 5% RH × 1 day |
||
After curing |
Density at 23°C g/cm3 |
1.02 |
Hardness Durometer A |
32 | |
Tensile strength MPa |
1.1 | |
Elongation at break % |
150 | |
Volume resistivity TΩ・m |
79 | |
Dielectric breakdown strength kV/mm |
28 | |
Relative permittivity 50Hz |
2.8 | |
Dissipation factor 50Hz |
4.3 × 10‒4 | |
Lap shear strength (Al/Al) MPa |
0.3 | |
Low-molecular-weight siloxane content |
300 ≥ |
Parameter ![]() |
X-31-2835-A/B | Two-component condensation-cure Conventional product |
Two-component addition-cure Conventional product |
||
---|---|---|---|---|---|
Room temperature 1 day |
Lap shear strength MPa |
PBT | 0.2 (80)* | 0.1 (0)* | 2.2 (100)* |
Al | 0.3 (100)* | 1.1 (100)* | 2.4 (100)* | ||
Hardness Durometer A |
32 | 35 | 20 | ||
Room temperature 3 days + |
Hardness Durometer A |
32 | 35 | 32 | |
Curing inhibitors |
Butyl rubber sheet (sulfer) |
Not inhibit curing | Not inhibit curing | Inhibit curing | |
Addition of amine |
Not inhibit curing | Not inhibit curing | Inhibit curing |
* Values in parentheses: cohesive failure rate