X-31-2835-A/B
Parameter  Product name |
X-31-2835-A/B | Two component condensation cure type Conventional product |
Two component addition cure type Conventional product |
||
|---|---|---|---|---|---|
| Room temperature 1 day |
Tensile lap-shear |
PBT | 0.2 (80)* | 0.1 (0) | 2.2 (100) |
| Al | 0.3 (100) | 1.1 (100) | 2.4 (100) | ||
Hardness Durometer A |
32 | 35 | 20 | ||
| Room temperature 3 days + Post cure 120°C×1h |
Hardness Durometer A |
32 | 35 | 32 | |
| Cure inhibition |
Butyl rubber (S) |
Cure | Cure | Not cured | |
Amine added (N) |
Cure | Cure | Not cured | ||
*Values in ()：Cohesive failure ratio
| Parameter Product name |
X-31-2835-A/B | |
|---|---|---|
By-product gas |
Alcohol | |
 |
Consistency |
Liquid |
Appearance |
A/B: Creamy white | |
Viscosity at 23°C Rotation number: 10s-1 Pa·s |
38/30 | |
Mix ratio |
100:100 | |
Pot life min |
9 | |
Standard curing conditions |
23°C ± 2°C / 50 ± 5% RH × 1 day | |
 |
Density at 23°C g/cm3 |
1.02 |
Hardness Durometer A |
32 | |
Tensile strength MPa |
1.1 | |
Elongation at break % |
150 | |
Volume resistivity TΩ·m |
79 | |
Dielectric breakdown strength kV/mm |
28 | |
Relative permittivity 50 Hz |
2.8 | |
Dielectric dissipation factor 50 Hz |
4.3 × 10-4 | |
Tensile lap-shear strength (Al/Al) MPa |
0.3 | |
LMW siloxane content ∑D3-D10 ppm |
300 ≥ | |